Divinycell H80 structural foam core | 1/4 sheet 1220x610mm

USD $56.75
usually ships within 2 business days
Calculated at checkout

Divinycell H provides excellent mechanical properties to low weight. The unique combination of polyuren and pvc, yields impressive mechanical performance. Divinycell H has been widely used and has a proven track record in virtually every application area where sandwich composites are employed including the marine (leisure, military and commercial), land transportation, wind energy, civil engineering/infrastructure and general industrial markets

Divinycell H is ideal for applications subject to fatigue, slamming or impact loads. Other key features of Divinycell H include consistent high quality, excellent adhesion/peel strength, excellent chemical resistance, low water absorption and good thermal/acoustic insulation. With its low thermal conductivity, Divinycell H is especially suitable as insulation for low and cryogenic temperatures. Resistance to hydrocarbons makes it the perfect material for LNG storage insulation.

Divinycell H is compatible with virtually all commonly used resins and manufacturing systems.

  • High temperature resistance
  • Low water absorption
  • Superior damage tolerance
  • Fast and easy to process
  • Good chemical resistance
  • Excellent fatigue properties
  • Low resin uptake
  • Wide range of properties
  • Provides excellent mechanical properties to a low weight

Other Details

Properties tested at 23 deg C:
Compressive strength:
1.15-1.4 MPa
Compressive modulus:
80-90 MPa
Tensile strength:
2.2-2.5 MPa
Tensile modulus:
85-95 MPa
Shear strength:
0.95-1.15 MPa
Shear modulus:
23-27 MPa
Shear strain:
Thermal conductivity (at 20 deg C):
.031 W/(m-K)
Heat distortion temperature:
+125 deg C
Continous temp range:
-200 to +70 deg C
Dielectric constant:
Poissons ratio: